Description
Epoxy resin systems
Low temperature, anti-crystallization
Component A：
Epoxy matrix
Without classified Toxic products (T)
Component B：
H-601 Fast hardener, phenol free
H-608 slow hardener
H-609 Ultra slow hardener
Profile:
Cure at ambiant temperature and post cure at 40 to 60℃
Packaging:
Component A：10kg
Component B：10kg
Parameters
Component A：
| Appearance | Viscous liquid | |
| Chemical nature | Epoxy resin. Reaction product between bisphenoland epichlorhydrine. | |
| Storage | Can crystallize at low temperature or after a longstorage. Shelf life : 2 years @ 18 – 25°C | |
| Color | Clear to yellow, Gardner < 3 | |
| Density (Kg/l)Picnometer NF EN ISO 2811-1 | @ 20 °C | 1.159 + 0.005 |
| Viscosities(m.Pas + 20 %) | @ 15 °C | 6380 ±1270 |
| @ 20 °C | 3240 ± 650 | |
| @ 25 °C | 1780 ±360 | |
| Rheometer CP 50 mmShear rate 10 s | @ 30 °C | 1040±210 |
| @ 40 °C | 410 ±80 | |
Component B：
| H-601 | H-608 | H-609 | ||
| Aspect / color | Amber Liquid | Clear Liquid | Clear Liquid | |
| Reactivity levels | Fast | Medium | Ultra slow | |
| Viscosities (m.Pas + 20 %) | @ 15 °C | 450±90 | 110±22 | 25±5 |
| @ 20 °C | 300±60 | 80±16 | 18±4 | |
| @ 25 °C | 200±40 | 60±12 | 15±3 | |
| Rheometer CP 50 mm Shear rate 10 s | @ 30 °C | 140±28 | 40±8 | 11±2 |
| @ 40 °C | 75±15 | 25±5 | 8±2 | |
| Density (g/cm3 + 0.005) Picnometer NF EN ISO 2811-1 | @ 20 °C | 1.073 | 0.952 | 0.948 |
Component A/Component B Mixes：
| H-601 | H-608 | H-609 | ||
| Viscosities (m.Pas + 20 %） Rheometer CP 50 mm Shear rate 10 s-1 | @ 20 °C | 1400 | 940 | 630 |
| @ 30 °C | 700 | 360 | 220 | |
| @ 40 °C | 350 | 210 | 120 | |
| Quantity by weight | 3：1 | |||
Levels of Reantivites on 100g mix Component A/Component B ：
| H-601 | H-608 | H-609 | ||
| Exothermic temperature (°C) | @ 20 °C | 215 | 200 | 22 |
| @ 30 °C | 215 | 210 | 40 | |
| @ 40 °C | 215 | 210 | 110 | |
| Time taken to achieve exotherm | @ 20 °C | 20min | 73min | 15h |
| @ 30 °C | 12min | 33min | 7h | |
| @ 40 °C | 7min | 19min | 3h | |
| Time taken to reach 50 °C | @ 20 °C | 13min | 63min | 17h |
| @ 30 °C | 9min | 23min | 9h | |
| @ 40 °C | 3min | 11min | 4h30 | |
Mechanical properties of pure resin:
| H-601 | H-608 | H-609 | ||||||
| Cure Schedule | 24h 23°C+24h 40°C | 24h 23°C+8h 60°C | 24h 23°C+24h 40°C | 24h 23°C + 16h 60°C | 24h 23°C + 24h 40°C | 24h 23°C + 16h 60°C | 24h 23°C + 8 h 80°C | |
| Tensile | ||||||||
| Modulus of elasticity | N/mm2 | 3250 | 3200 | 3150 | 3050 | 2750 | 2400 | 2300 |
| Maximum resistance | N/mm2 | 76 | 79 | 77 | 77 | 66 | 64 | 54 |
| Resistance at break | N/mm2 | 75 | 73 | 76 | 74 | 63 | 59 | 46 |
| Elongation at max.resistance | % | 3.6 | 4.2 | 3.4 | 4.0 | 3.1 | 3.9 | 4.9 |
| Elongation at break | % | 3.8 | 5.7 | 3.5 | 4.8 | 3.4 | 4.8 | 9.6 |
| Flexion | ||||||||
| Modulus of elasticity | N/mm2 | 3450 | 3250 | 3200 | 3100 | 3100 | 2800 | 2500 |
| Maximum resistance | N/mm2 | 125 | 124 | 120 | 119 | 103 | 99 | 87 |
| Elongation at max.resistance | % | 4.9 | 5.6 | 4.5 | 5.5 | 4.1 | 5.0 | 5.5 |
| Elongation at break | % | 9.3 | 8.2 | 10.0 | 9.0 | 11.5 | 9.3 | 13.0 |
| Charpy impact strength | ||||||||
| Resilience | KJ/mm2 | 20 | 29 | 24 | 35 | 28 | 40 | 37 |
| Glass Transition / DSC | ||||||||
| Tg 1 | ℃ | 65 | 77 | 65 | 79 | 65 | 79 | 85 |
| Tg 1 max | ℃ | / | 80 | / | 84 | / | / | 87 |
Tests carried out on samples of pure cast resin, without prior degasing, betwween steel plates.
Measures undertaken according to Afnor normes :
Tension: NF T 51-034
Flexion : NF T 51-001
Choc Charpy: NF T 51-035
Glass transition DSC : Onset - Tg1: 1stpoint @ 20 ℃/ mn,
Tg 1 max.: 2nd passage 180 ℃ under nitrogen gaz
ISO 11357