Advantages of Carbon Fiber Fabric
Lightweight Performance
Density: 1.5–2 g/cm³ (1/4 of steel, 1/3 of aluminum) → 30–70% weight reduction
Ideal for automotive, drones, sports equipment — enhances mobility & energy efficiency
Strength Exceeding Steel
Tensile strength: 3,000–7,000 MPa (5x–10x stronger than steel)
Exceptional fatigue resistance → extends service life of wind turbine blades, robotic arms
Extreme Environment Adaptability
Withstands -50°C to 300°C → aerospace components, brake systems
Acid/alkali corrosion resistance → durable solutions for chemical plants & marine engineering
Multifunctional Potential
Conductive/Thermal-modified variants (e.g., semiconductor equipment parts)
X-ray radiolucency → medical CT tabletops: 50% lighter with zero imaging interference
Primary Application Fields:
Aircraft fuselages, satellite components, rocket nozzles → Weight reduction enhances fuel efficiency (e.g., Boeing 787: 50% carbon fiber composites)
High-performance bodies (F1 racing cars), EV battery enclosures → Balances lightweight design with crash safety
Golf clubs, bicycle frames, tennis rackets → Increases strength & reduces athlete fatigue
Armor materials, UAV airframes, missile casings → Combines lightweight properties with impact resistance
Corrosion-resistant marine structures, ship hulls → Withstands saltwater/acid-alkali erosion
EMI shielding housings; medical imaging devices (e.g., X-ray tabletops) → Eliminates interference & metal artifacts
The following displays the basic information of the fabric
| Item | Data | Tolerance |
| Weaving method | Unidirectional | / |
| Fiber surface density (g/m ²) | 200 | ±10% |
| Resin content (%) | 33 | ±5 |
| Prepreg material surface density (g/m ²) | 299 | ±10% |
| width（mm） | 1000~1500 | -0+10 |
| Thickness (mm) | 0.2 | ±0.05 |
| raw material | T700-12KCarbon Fiber | / |
| molding condition | 150℃×30min | / |
The following displays the performance of raw materials
| item | Standard | Testing standards |
| Linear density (g/km) | 800±6 | GB/T 3362-2017 |
| density (g/cm³) | 1.80±0.02 | B/T 30019-201 |
| Tensile strength (MPa) | ≥4900 | GB/T 3362-2017 |
| Tensile modulus of elasticity (GPa) | ≥230 | B/T 3362-2017 |
| Tensile elongation at break (%) | ≥2.1 | B/T 3362-2017 |
Product Technical Parameters
| Serial number | Specification model code | Weaving method | Fiber surface density g/㎡ | Resin content | Prepreg surface density g/㎡ | Width (mm) | Theoretical thickness mm | raw materials |
| 1 | BYPrepreg-24UC CF12 | unidirectional | 24 | 45 | 44 | 100~1000 | 0.03 | T700-12K carbon fiber tensile strength: 4900MPa tensile modulus: 230GPa |
| 2 | BYPrepreg-30UC CF12 | unidirectional | 30 | 40 | 50 | 100~1000 | 0.03 | |
| 3 | BYPrepreg-40UC CF12 | unidirectional | 40 | 37 | 63 | 100~1000 | 0.04 | |
| 4 | BYPrepreg-50UC CF12 | unidirectional | 50 | 37 | 79 | 100~1000 | 0.05 | |
| 5 | BYPrepreg-55UC CF12 | unidirectional | 55 | 37 | 87 | 100~1000 | 0.06 | |
| 6 | BYPrepreg-75UC CF12 | unidirectional | 75 | 37 | 119 | 100~1000 | 0.08 | |
| 7 | BYPrepreg-100UC CF12 | unidirectional | 100 | 33 | 149 | 100~1000 | 0.10 | |
| 8 | BYPrepreg-125UC CF12 | unidirectional | 125 | 33 | 187 | 100~1000 | 0.12 | |
| 9 | BYPrepreg-150UC CF12 | unidirectional | 150 | 33 | 224 | 100~1000 | 0.14 | |
| 10 | BYPrepreg-175UC CF12 | unidirectional | 175 | 33 | 261 | 100~1000 | 0.17 | |
| 11 | BYPrepreg-200UC CF12 | unidirectional | 200 | 33 | 299 | 100~1000 | 0.19 | |
| 12 | BYPrepreg-30UC CF12 S | unidirectional | 30 | 40 | 50 | 100~1000 | 0.03 | T800 grade carbon fiber tensile strength: 5880MPa tensile modulus: 294GPa |
| 13 | BYPrepreg-40UC CF12 S | unidirectional | 40 | 37 | 64 | 100~1000 | 0.04 | |
| 14 | BYPrepreg-50UC CF12 S | unidirectional | 50 | 37 | 79 | 100~1000 | 0.05 | |
| 15 | BYPrepreg-55UC CF12 S | unidirectional | 55 | 37 | 87 | 100~1000 | 0.06 | |
| 16 | BYPrepreg-75UC CF12 S | unidirectional | 75 | 37 | 119 | 100~1000 | 0.08 | |
| 17 | BYPrepreg-100UC CF12 S | unidirectional | 100 | 24 | 132 | 100~1000 | 0.08 | |
| 18 | BYPrepreg-125UC CF12 S | unidirectional | 125 | 24 | 164 | 100~1000 | 0.10 | |
| 19 | BYPrepreg-150UC CF12 S | unidirectional | 150 | 33 | 225 | 100~1000 | 0.14 | |
| 20 | BYPrepreg-175UC CF12 S | unidirectional | 175 | 33 | 261 | 100~1000 | 0.17 | |
| 21 | BYPrepreg-200UC CF12 M | unidirectional | 200 | 33 | 299 | 100~1000 | 0.19 | M40 grade carbon fiber tensile strength: 44000MPa tensile modulus: 377GPa |
| 22 | BYPrepreg-30UC CF12 M | unidirectional | 30 | 40 | 50 | 100~1000 | 0.03 | |
| 23 | BYPrepreg-40UC CF12 M | unidirectional | 40 | 37 | 64 | 100~1000 | 0.04 | |
| 24 | BYPrepreg-50UC CF12 M | unidirectional | 50 | 37 | 79 | 100~1000 | 0.05 |
* Square weight tolerance ±10%; width tolerance -0+10mm; thickness tolerance ±0.05mm
Customization scope:
width
fiber surface density
weaving method
raw materials
resin content